Select All Heat deflection temperature
(0.45Mpa)
Heat distortion temperature
(1.8Mpa)
Short-term maximum temperature Continuous use temperature Thermal conductivity Coefficients of linear expansion Combustion
ABS 98 80 95 65 0.16 9.22 HB
PVC 75 75 70 60 0.165 7 HB
CPVC 60 90 100 90 0.145 5.98 HB
HPVC 60 60.66 80 61/-40 0.1888 .654 HB
PU 110 80 90 70 0.566 6.11  
HDPE 80 85 100 83/-49 0.55 14.06 HB
UPE 85 85 100 85 0.41 19.9 HB
PP-H 105 80 105 90 0.11 7.75 HB
PMMA 85 90 80 83/-40 0.1443 6.22 HB
PC1000 140 140 150 117/-151 0.21 6.88 V-2/HB
PC 141 141 136 117/-150 4.6 7.0 V-0
PC-GF20 149 145 133 130 0.20 2.6 V-1
POM-C 158 158 120 90/-50 0.234 8.47 HB
POM-H(Delrin) 170 124 150 86 0.38 12.22 HB
Nylon 6 205-219 205-219 160 92/-30 0.23 7.3 HB
MC-Graphite Powder 190 92 150 92   7.4  
MC-MOS2 189 92 148 95/-20   7.3  
MC-MOS2-Oil   95 164 94   8.2 HB
MC-Oil 176 90 165 106/-20 0.22 7.3 HB
MC-Lube   95 152 95   9.8  
MC901 222 94 160 120 0.25 9.0 HB
MC907   95   95 0.23 8 HB
PA6 NYLON 189 73 220 85/70 0.22 9 HB
PA6-GF30 222 212 180 100 0.26 2.7 HB
PA6-MOS2     170 100   9.6 HB
PA66-GF30 255 251 240 111 0.25 4 HB
PA66-MOS2(GS) 244 91 180 111 0.24 7.3 HB
PTFE 260 80 317-327 180~270 5.9 11.8 V-0
PTFE(Etched) 142 55 285 180~270 0.25 11.8 V-0
PTFE-CF25     320 260/-240 0.74 14.6  
PTFE-GF     320 260/-240 0.44 9.8  
PTFE-MOS2 142 54 316 260 0.24 11.8 V-0
PTFE-Graphite 142 54 316 260 0.24 11.8 V-0
PTFE-RYT     314 260 0.41 9.9  
PVDF (2F) 160 160 160 160 0.20 10E-5 V-0
PETP 166 80 158 116 0.30 7 HB
PETP     158 116   7 HB
PSU1000 180 173 180 150 0.25 5.57 HB
ULTEM-PEI 211 200 200 170 0.11 5.59 V-0
PPS-1000 205 113 258 222 0.21 2.5 V-0
PPS-GF40   258 258 222 0.21 1.6 V-2
PPS-PVX(HPV)   114 260 220     V-0
PEEK 210 141 310 250 0.25 4.68 V-0
PEEK-CF30   315 287 258 0.91 1.43 V-0
PEEK-GF30 342 315 310 250 0.42 2.15 V-0
PEEK-PVX(HPV) 292 276 310 250 0.23 2.3 V-0
Torlon PAI-4203 280 277 270 250 0.28 3.2 V-0
Torlon PAI-4301   280 270 250 0.7 2.4 V-0
Torlon PAI-5530   270 270 250 0.35 3.9 V-0
PBI   426 540 345 0.3 2.35 V-0
PHENOLIC X PEPER 80 80 182 128 50 1.2 HB
PHENOLIC XPC PEPER     178 132     HB
PHENOLIC XX PEPER     178 132     HB
PHENOLIC XXX PEPER     182 128   1.48 HB
PHENOLIC C     180 124 0.37 2.15 HB
PHENOLIC CE     180 124 0.37 2.06 HB
FRP 310 380 230 180~200     V-0
MICA (MUSCOVITE)     952 652 0.2 7 V-0
MICA (SILICONE RESIN) 550 560 700 1000 0.2 7 V-0
MICA (EPOXY RESIN)     700 1000 0.2 7 V-0
Starlint     391 262 0.23 6.7  
POM-CN   81 140 90/-50   7 HB
POM-AS 130 87 140 90/-50 0.32 11.8 HB
MC501-R2 181     120/-30 0.52 9  
MC501-R6 181   180 120/-30 0.72 7.6  
PPS-CN   174 165 95   9.0 HB
PPS-SD   167 258 222     V-0
PEEK-CN     300 258 0.28 1.6 V-0
Esd225(POM)   106 140 90   16.73 HB
Esd410(C)(Ultem PEI)   211 200 170 0.36 3.23 V-0
Esd420(Ultem PEI)   217 220 170 0.21 3.6 V-0
Esd480(PEEK)   262 300 245 0.24 3.2  
Esd520HR(PAI)   270 270 250 0.35 4.24 V-0
CFRP4     2200 20~2000      
CAS761 300 300 360 300 0.3 10 V0
CAG762 250 250 360 300 0.3 10 VO
CCR766     360 300 0.3 10  
ISOLA CDM 300 300 360 300 0.3 10 VO